From the blog

RongxinGroup is China’s leading supplier of graphite electrode and electrode paste.

VIEW POST
The van in the factory
2018-09-19 10:06:01
|
3 comments
The van in the factory
VIEW POST
bc
2018-09-17 10:20:18
|
3 comments
bc
VIEW POST
hi
2018-09-13 10:21:00
|
3 comments
hi
VIEW POST
h
2018-09-12 09:46:33
|
3 comments
h
VIEW POST
g
2018-09-10 10:19:15
|
3 comments
g
VIEW POST
Labeled graphite electrode
2018-09-07 11:34:14
|
3 comments
Labeled graphite electrode
VIEW POST
Graphite electrode loading
2018-09-06 17:05:37
|
3 comments
Graphite electrode loading
VIEW POST
Full process plant
2018-09-05 10:26:00
|
3 comments
Full process plant
VIEW POST
Finished graphite electrode
2018-09-03 12:57:06
|
3 comments
Finished graphite electrode
VIEW POST
truck
2018-08-30 10:37:41
|
3 comments
truck

HOT SELLING

well selled in the latest days.

UHP Graphite Electrodes
Resistance:4.8-5.8
Density:>1.68
CTE:1.1-1.4
Young Modulue:9.0-13.0
Rupture Modulus:10.0-14.0
HP Graphite Electrodes
Resistance:5.8-6.6
Density:>1.62
CTE:1.4-2.2
Young Modulue:13.0-16.0
Rupture Modulus:10.0-11.0
RP Graphite Electrodes
Resistance:6.6-9.0
Density:>1.53
CTE:1.4-2.2
Young Modulue:9.0-13.0
Rupture Modulus:11.0-15.0
Goose Shaped & Trapezoid Shaped
Goose Shaped:30mm*60mm*80mm;
Trapezoid Shaped:Bottom Length14cm,Bottom Wieth 10cm;Height 9.5cm;Top Legnth 9cm,Top Width 4cm.
Ash content 2-10%
Resistivity 55-90 uΩm
V.M 10.0-15.0
Density >1.46g/cm3
Compression Strength >18Mpa
Extensibility 6-20
Carbon Electrode Paste(Cylinder)
Diameter:600mm;
Length:1000mm;
Ash content 2-10%
Resistivity 55-90 uΩm
V.M 10.0-15.0
Density >1.46g/cm3
Compression Strength >18Mpa
Extensibility 6-20
Various types of electrode paste
petroleum coke, asphalt in the melting bath dehydration, melting, in proportion to join the HunNieGuo kneading, and then formed calcined together.With the characteristics of low resistance coefficient used in the electric equipment such as ferroalloys fur
Various types of electrode paste
petroleum coke, asphalt in the melting bath dehydration, melting, in proportion to join the HunNieGuo kneading, and then formed calcined together.With the characteristics of low resistance coefficient used in the electric equipment such as ferroalloys fur
Electrode paste
petroleum coke, asphalt in the melting bath dehydration, melting, in proportion to join the HunNieGuo kneading, and then formed calcined together.With the characteristics of low resistance coefficient used in the electric equipment such as ferroalloys fur
Cylindrical electrode paste
petroleum coke, asphalt in the melting bath dehydration, melting, in proportion to join the HunNieGuo kneading, and then formed calcined together.With the characteristics of low resistance coefficient used in the electric equipment such as ferroalloys fur