From the blog

RongxinGroup is China’s leading supplier of graphite electrode and electrode paste.

VIEW POST
factory
2018-08-29 11:28:58
|
3 comments
factory
VIEW POST
graphite electrode factory
2018-08-28 11:44:14
|
3 comments
graphite electrode factory
VIEW POST
customers look at the factory
2018-08-27 11:08:56
|
3 comments
customers look at the factory
VIEW POST
c
2018-08-24 09:49:31
|
3 comments
c
VIEW POST
Electrode Paste Finished Product
2018-08-22 10:46:12
|
3 comments
Electrode Paste Finished Product
VIEW POST
b
2018-08-21 10:43:56
|
3 comments
b
VIEW POST
a
2018-08-20 10:32:18
|
3 comments
a
VIEW POST
Bagged Seal
2018-08-17 10:56:42
|
3 comments
Bagged Seal
VIEW POST
The Best Price Graphite Electrode
2018-08-15 14:39:24
|
3 comments
The Best Price Graphite Electrode
VIEW POST
Electrode Paste
2018-08-08 10:52:44
|
3 comments
Electrode Paste

HOT SELLING

well selled in the latest days.

UHP Graphite Electrodes
Resistance:4.8-5.8
Density:>1.68
CTE:1.1-1.4
Young Modulue:9.0-13.0
Rupture Modulus:10.0-14.0
HP Graphite Electrodes
Resistance:5.8-6.6
Density:>1.62
CTE:1.4-2.2
Young Modulue:13.0-16.0
Rupture Modulus:10.0-11.0
RP Graphite Electrodes
Resistance:6.6-9.0
Density:>1.53
CTE:1.4-2.2
Young Modulue:9.0-13.0
Rupture Modulus:11.0-15.0
Goose Shaped & Trapezoid Shaped
Goose Shaped:30mm*60mm*80mm;
Trapezoid Shaped:Bottom Length14cm,Bottom Wieth 10cm;Height 9.5cm;Top Legnth 9cm,Top Width 4cm.
Ash content 2-10%
Resistivity 55-90 uΩm
V.M 10.0-15.0
Density >1.46g/cm3
Compression Strength >18Mpa
Extensibility 6-20
Carbon Electrode Paste(Cylinder)
Diameter:600mm;
Length:1000mm;
Ash content 2-10%
Resistivity 55-90 uΩm
V.M 10.0-15.0
Density >1.46g/cm3
Compression Strength >18Mpa
Extensibility 6-20
Various types of electrode paste
petroleum coke, asphalt in the melting bath dehydration, melting, in proportion to join the HunNieGuo kneading, and then formed calcined together.With the characteristics of low resistance coefficient used in the electric equipment such as ferroalloys fur
Various types of electrode paste
petroleum coke, asphalt in the melting bath dehydration, melting, in proportion to join the HunNieGuo kneading, and then formed calcined together.With the characteristics of low resistance coefficient used in the electric equipment such as ferroalloys fur
Electrode paste
petroleum coke, asphalt in the melting bath dehydration, melting, in proportion to join the HunNieGuo kneading, and then formed calcined together.With the characteristics of low resistance coefficient used in the electric equipment such as ferroalloys fur
Cylindrical electrode paste
petroleum coke, asphalt in the melting bath dehydration, melting, in proportion to join the HunNieGuo kneading, and then formed calcined together.With the characteristics of low resistance coefficient used in the electric equipment such as ferroalloys fur